Maqolada dispers wollastonit va bazalt fibraning birgalikdagi qo‘llanilishi natijasida avtoklavsiz sement–kul ko‘pikbetonning kuchlanish-deformatsion holati, g‘ovaklar spektri va ekspluatatsion barqarorligi o‘rganildi. Nazorat tarkib bilan taqqoslaganda dispers wollastonit kiritingan tarkibda 28 sutkalik mustahkamlik 1,30 MPa dan 1,78 MPa gacha oshdi, baza tarkibiga bazalt fibra ham qo‘shilganda ushbu ko‘rsatkich 1,92 MPa ga yetdi. Kirishish deformatsiyasi 1,12 mm/m dan 0,82 mm/m gacha pasaydi, yopiq g‘ovaklik ulushi esa 46% dan 52% gacha ortdi. Natijalar mikroarmirlash va g‘ovaklararo to‘siqlar zichlanishi tufayli yoriq hosil bo‘lish markazlari kamayishi bilan izohlandi.
АННОТАЦИЯ. В статье исследованы напряжённо-деформированное состояние, спектр пористости и эксплуатационная устойчивость неавтоклавного цементно-зольного пенобетона при совместном применении дисперсного волластонита и базальтовой фибры. По сравнению с контрольным составом в составе с введением дисперсного волластонита 28-суточная прочность при сжатии увеличилась с 1,30 МПа до 1,78 МПа, а при дополнительном введении базальтовой фибры в базовый состав данный показатель достиг 1,92 МПа. Усадочная деформация снизилась с 1,12 мм/м до 0,82 мм/м, при этом доля закрытой пористости увеличилась с 46% до 52%. Полученные результаты объясняются снижением количества центров трещинообразования за счёт микроармирования и уплотнения межпоровых перегородок.
ANNOTATION. The article investigates the stress–strain behavior, pore-size distribution, and operational stability of non-autoclaved cement–fly ash foam concrete produced with the combined use of finely dispersed wollastonite and basalt fiber. Compared with the control composition, the 28-day compressive strength of the mix containing finely dispersed wollastonite increased from 1.30 MPa to 1.78 MPa. When basalt fiber was additionally introduced into the base composition, this value reached 1.92 MPa. Shrinkage deformation decreased from 1.12 mm/m to 0.82 mm/m, while the proportion of closed porosity increased from 46% to 52%. The obtained results were attributed to a reduction in crack initiation centers due to micro-reinforcement and the densification of interpore partitions.
Kalit so’zlar: bazalt fibra, dispers wollastonit, sinergiya, kirishish, yopiq g‘ovaklik, ekspluatatsion barqarorlik, ko‘pikbeton.
Ключевые слова: базальтовая фибра, дисперсный волластонит, синергия, усадка, закрытая пористость, эксплуатационная устойчивость, пенобетон.
Key words: basalt fiber, finely dispersed wollastonite, synergy, shrinkage, closed porosity, operational stability, foam concrete